Effect of Nano-Silica on the Mechanical and Durability Properties of Concrete: A Comprehensive Review

Abstract

The incorporation of nanotechnology has led to significant strides in the concrete industry, ushering in innovative construction methodologies. Various nanomaterials, including nano-silica (NS), have undergone comprehensive scrutiny as potential partial substitutes for cement in concrete formulations. This article aims to provide a comprehensive overview of the impacts of NS on several mechanical properties of concrete, encompassing compressive, split tensile, and flexural strengths. Additionally, the review delves into the influence of NS on the concrete’s durability, including microstructural characterization and the eradication of structural micropores. NS has demonstrated the capacity to bolster both strength and durability while concurrently diminishing structural micropores. Moreover, this review explores the contemporary status of NS application in cement concrete and presents avenues for prospective research. The assessment of engineering attributes becomes imperative for concrete infused with nano-silica. This encompasses aspects like bond strength, creep, shrinkage, and more. A rigorous evaluation of fresh and hardened properties is necessary to discern the material’s thermal and acoustical characteristics. Such a comprehensive understanding contributes to a holistic evaluation of the material’s adaptability across diverse applications.

Introduction

I. INTRODUCTION

Concrete has undergone significant changes since its inception, starting with normal concrete. In the 1900s, this concrete form was often utilized for construction projects since it offered adequate strength for all uses [1]. Normal concrete contained fewer than 380 kg/m3 of cement, typical aggregates, moderate water requirements, and a small amount of superplasticizers [2]. However, the emergence of unique structural designs in the 1960s required concrete with a high load-bearing capacity, exceeding 50 MPa up to 95 MPa [3]. High Strength Concrete (HSC) was developed to meet this demand, which can bear loads ranging from 50 MPa to 90 MPa [4]. More cement, more aggregate, less water, and suitable superplasticizers are needed for HSC. Various additives and extra materials were introduced to do this, including nano-silica, fly ash, metakaolin, and other pozzolanic minerals [5,6].

Employing nanoparticles to improve the mechanical behavior of cementitious compos- ites was originally explored in the late 1980s, and research in this field has been ongoing for almost two decades [7].

Due to their remarkable qualities and capabilities, nanomaterials can improve the behavior of concrete [8–10]. Nano-SiO2 is one of the most widely used nanomaterials, made up of pozzolanic materials that can react with cement hydration products [11].

Incorporating Nano-SiO2 improved cement-based performance, such as compressive, flexural strength, water penetration resistance, sulfate attack, and reduced calcium leaching [11–13].       

Nanotechnology has experienced significant progress, leading to noteworthy find- ings concerning particles smaller than 100 nm [14]. These minute particles can aug- ment the mechanical characteristics of diverse materials, including polymers [15] and concrete [16]. Additionally, they hold relevance in various sectors, such as engineering, food, and medicine [17]. Therefore, researchers have concentrated on examining the ef- fects of nano-silica in concrete [18].

Several nanoparticles have been studied, including nano titanium dioxide, nano aluminum oxide, nano iron oxide, nano zinc oxide, and nano-silica [18,19].

According to studies, adding nano-silica to concrete can greatly improve the compres- sive strength of the material [20]. Additionally, it has been demonstrated that nano-silica can shorten the initial and final setting while accelerating the concrete’s early-age strength.

This is clarified via the point that nano-silica has a big specific surface area and serves as a solid binder between cement and aggregate [21,22]. Additionally, due to its extremely small particle size, nano-silica exhibits excellent pozzolanic activity [23,24], enabling it to completely fill in all the pores and voids in concrete, including the Interfacial Transition Zone (ITZ), thereby enhancing its strength [20,25,26].

Furthermore, introducing nano-silica enhances calcium silicate hydrate (C-S-H) gel formation, a critical component for concrete strength. This increased concrete hydration, as studied by Norhasri et al. (2017) [27], Barbhuiya et al. (2020) [16], and Mohammed et al. (2018) [28], leads to a higher C-S-H gel content. Simultaneously, the reaction between nano-silica and portlandite-Ca(OH)2 reduces the concrete’s portlandite content, resulting in a denser concrete structure. Despite numerous studies on the impact of nano-silica on concrete, there is a lack of comprehensive research that covers all its effects in a single document.

This study aims to bridge that gap by thoroughly investigating the concrete’s mechanical characteristics, durability, and microstructural characteristics containing nano-silica. The analysis is based on a meticulous review of approximately one hundred research papers demonstrating nano-silica’s diverse impacts on concrete.

II. NANOMATERIALS

Nanomaterials are materials that have been decreased in component to a range of 1–100 nm or contain at least a single dimension inside this nanoscale range in a three- dimensional space. Nanostructured materials and nanostructured components are the two main subcategories of nanomaterials.

While nanostructured components have at least one structural component with an outside dimension inside the nanometer range, nanostructured materials are distinguished by having structural dimensions that are in the nanoscale range. This categorization is based on the external dimensions of the structural elements of the materials. [29,30].

Nanomaterials possess unique characteristics that set them apart from conventional materials. For instance, cement mortar incorporating nano- silica or nano-Fe2O3 demonstrated increased strength in compression and flexure after 28 days of measurement compared to the blank group, indicating an improved performance due to the inclusion of nanomaterials [31]. Similarly, nano-Al2O3 ceramics exhibited higher flexural strength than micro-scale monolithic alumina ceramics, highlighting the enhanced mechanical properties of nanomaterials [32].

Table 1 presents the types of nanomaterial particles documented in the literature  Nanoparticles possess unique mechanical properties that arise from their volume, surface, and quantum effects.

When added to a material, they result in a smaller grain size, resulting in the formation of an intragranular or intergranular structure.

This, in turn, improves the quality of the grain border as well as enhances the physical characteristics of the material [45]. When nanoparticles are added, they dramatically increase the mechanical characteristics of numerous materials. Illustratively, the augmentation of mechanical properties in materials via nanoparticles is evident in the work of Saba et al. (2016) [46]. Their study demonstrated a notable enhancement in mechanical behavior by incorporating a 3% nanoscale oil palm hollow fruit fiber filler into kenaf epoxy alloys.

A significant stride has been made in understanding the mechanical characteristics of metal nanomaterials. Table 2 presents detailed information on the physical characteristics of nanomaterials.

The higher performance of nanocomposites containing metal nanoparticles over mono- lithic Al2O3 is proof that, according to [47], the addition of metal nanoparticles to nanoma- terials increases their fracture toughness and strength. Metal particle pinning inhibits the formation of the Al2O3 matrix, resulting in a lower grain size and grain refining, which eventually improves the mechanical characteristics. In nanocomposites containing nano- Cu, the resulting hardness is less than that of Al2O3 because of the lower stiffness of Cu compared to Al2O3. However, in contrast, nanocomposites with nano-Ni-Co show an upper hardness than Al2O3 because of the greater toughness of Ni-Co relative to Al2O3. The final three data sets in Table 2 show that hybrid materials outperform single-reinforced composites in maximum toughness, impact resistance, and final tensile strength, which is most likely because of the reaction of SiC and B4C. These findings underscore the impact of metal nanoparticles on the structural behavior of nanomaterials

Table 3 presents the physical properties of nonmetallic nanomaterials. The mechanical properties of skutterudites decrease with the inclusion of carbon nanotubes in the resulting nanocomposite. It is hypothesized that the reduction in the physical characteristics of the resulting nanocomposite is produced via the construction of agglomerates of nanotubes made of carbon within the skutterudites. These agglomerates can operate as planes of slip that promote fracture propagation, lowering the nanocomposite’s overall mechanical performance. As a result, sample fracturing occurs even at modest mechanical stresses, as described by Schmitz et al. (2017) [49]. Contrarily, most organic nanostructures are flexible and lack mechanical characteristics like hardness and compressive strength. The last five entries in Table 3 show a decrease in tensile strength as the concentration of nano-HA increases, which may be due to a poor boundary between nano-HA and nano-PLLA. With the addition of nano-HA, the flexural strength of the nanocomposites first rises, then falls beyond a certain threshold. The maximum bending strength of 156.8 MPa is attained at a nano-HA content of 20%

In recent years, there has been an increasing use of silica nanoparticles, also called nano-silica or silicon dioxide nanoparticles, as a supplement to improve the physical and long-lasting qualities of concrete [51]. Research has demonstrated that including nano-silica into cement paste can enhance the concrete’s durability by improving its nanostructure, as stated by [52]. Furthermore, Ref. [53] found that nano-silica can be a viable option to reduce cement consumption in the production of high-strength concrete (HSC), thereby enhancing cost-effectiveness and reducing the material’s carbon footprint According to research by [54], nano-silica exhibits superior performance in terms of the filling effect and particle size distribution compared to conventional mineral admix- tures. Incorporating nano-silica into concrete mixtures reduces porosity and enhances the pozzolanic breakdown of nano-silica with calcium hydroxide, causing the production of CSH and enhancing the mechanical properties. Additionally, research has shown that nano-silica can develop the cement setting process and enhance the cohesiveness of fresh mixes, as noted by [55]. Kumar et al. (2019) [56] have stated that nano-silica has high pozzolanic action, which accelerates the cement hydration at an early stage, leading to the conversion of calcium hydroxide into CSH gel, thereby improving the physical characteristics of concrete. Additionally, Figure 1a,b depicts, respectively, the morphology of nano-silica in powdered form and when seen via electron transmission microscopy

III. MECHANICAL PROPERTIES

A. Compressive Strength

Table 4 compiles the findings from multiple studies that have investigated the com- pressive strength of concrete. One such study by Chithra et al. (2016) [36] noted that the addition of 2 weight percent of nano-silica to concrete, caused a 43% rise in compressive strength after 1 day and a 27% rise after 28 days, compared to standard concrete. However, the researchers cautioned against using excessive amounts of nano-silica, as it may lead to the aggregation of particles in the cement matrix, weakening the bonds within the matrix.

Elkady et al. (2019) [59] studied how different nano-silica dosages affected the struc- tural behavior of concrete. The findings revealed that using a 4.5% dosage of nano-silica caused a 13.5% rise in the compressive strength after seven days, compared to the standard group. For 1.5% and 3% nano-silica dosages, the strength gains were 3% and 4.5%, respec- tively. After 28 days, the strength gains were 17.5% and 29% at 1.5% and 4.5% nano-silica dosages, respectively, and a 43.5% increase in strength was observed at a 3% nano-silica dosage. According to [59], the study suggested that nano-silica particles agglomerated and prolonged the interaction time with the excess (CH), leading to the creation of CSH gel. These aggregated particles served as fillers, lowering porosity and boosting strength at an early age.

In comparison to the control group, the optimal dose of nano-silica was determined to be 3%, which boosted the binding strength by 38.5%. Yonggui et al. (2020) [60] studied the impact of different proportions of nano-silica replacements on the structural behavior of recycled aggregate concrete. Their research revealed that increasing the percentage of nano-silica replacements led to a decrease in compressive strength.

They also found that higher temperatures during the production of recycled concrete, where nano-silica replaced cement, adsorbed and capillary water, resulting in gas pressure that weakened the concrete’s interior micro-structure. In contrast, Alhawat and Ashour (2020) [61] noted that adding 1.5% nano- silica to concrete instead of cement boosted bond strength and corrosion resistance. Deb et al. (2015) [62] conducted research on the effect of nano-silica on geopoly- mer concrete and found that adding it increased the compressive strength by 2%, which matched to the control group.

However, using more than 2% nano-silica led to the presence of unreactive particles, which weakened the concrete considerably. Adak et al. (2014) [63] stated that adding 6% nano-silica to geopolymer mortar improved its mechanical prop- erties compared to normal cement mortar. Refs. [63,64] observed positive impacts on the physical characteristics of geopolymer concrete with the addition of 1% micro-silica and 2% nano-silica.

Mustakim et al. (2021) [65] discovered that adding 1.5% nano-silica, in addition to silica fume, to geopolymer concrete improved the microstructure and resulted in outstanding strength under compression, presumably because of the quick alkali activation process of geopolymer concrete.

Jalal et al. (2015) [66] conducted a study demonstrating that the incorporation of 2% nano-silica in high-performance self-compacting concrete resulted in a substantial enhancement in its strength and durability when matched to the control group. Chithra et al. (2016) [36] similarly found that the substitution of cement with 2% colloidal nano- silica improved the structural behavior of HPC. Ghafari et al. (2014) [67] reported that using 3% nano-silica as a cement replacement in ultra-high-performance concrete

resulted in an optimal performance by optimizing the pore structure and reducing the number of capillary holes, thereby improving the concrete’s performance.

Multiple research studies have explored the potential benefits of incorporating nano- silica to enhance the structural behavior of HPC. Fallah and Nematzadeh (2017) [68] dis- covered that adding 2% nano-silica and 12% silica fume to cement improved the structural behavior of HPC. Similarly, Amin & Abu el-Hassan (2015) [33] used nano-silica, Cu, and Ni ferrite to create high-strength concrete with improved mechanical qualities.

The increased amount of CSH gel that resulted from the nanoparticles’ interaction might account for the higher strength seen in these trials.

According to [69], fiber-reinforced concrete with desirable mechanical properties can be achieved by adding 8% silica fume and 1% steel fibers, which prevent crack formation and enhance the material’s performance. The study also found that substituting 2% of the cement with nano-silica further contributed to these benefits by promoting the production of more CSH gel and enhancing the concrete’s strength.

B. Tensile Strength

Adding nano-silica to concrete has been shown to increase its split tensile strength, according to research. Khaloo et al. (2016) [57] conducted an experiment on concrete using various sizes of nano-silica particles and discovered that 12 nm nano-silica was more effective at enhancing strength than 7 nm nano-silica. The study also suggested that the lower specific surface area of the 12 nm nano-silica facilitated better dispersion in water. Fallah and Nematzadeh (2017) [68] examined the influence of the addition of nano- silica to concrete on its splitting tensile strength. Results indicated that substituting 3% of cement with nano-silica headed to a 16.10% rise in tensile strength compared to regular concrete. However, the reinforcing effect of silica fume was found to be stronger than that of nano-silica. Furthermore, when 4% of nano-silica was added to concrete when compared to unaltered concrete, it resulted in a 35% rise in splitting tensile strength.

According to Zhang et al. (2019) [76], the incorporation of nano-silica in concrete provides both a form of nano-reinforcement and fills the porosity in the concrete matrix. Figure 2 compares the tensile strength of concrete when 3% nano-silica is utilized with a. 0.4 w/c ratio on various days.

The fact that nano-silica can both reinforce the concrete matrix and fill the porosity in the material is a promising characteristic for its use in concrete production. The comparison of tensile strength at different ages in Figure 2 provides evidence of the short-term durability of the nano-silica-modified concrete Overall, the results indicate that adding nano-silica to concrete may be a practical way to increase its split tensile strength, a crucial mechanical characteristic for withstanding tensile stresses and preventing material splitting. The enhancement of the concrete’s tensile strength is driven via multiple mechanisms. These encompass heightened bonding among nano-silica, cement, and aggregates; the filling of voids between cement particles and surrounding aggregates (a micro-filling effect that diminishes microcrack count and size); refining the interfacial transition zone (ITZ) by minimizing weak points and voids; the capacity for reducing the water-cement ratio due to the water-reducing effects; and a pozzolanic reaction between nano-silica and calcium hydroxide, leading to the creation of supplementary C-S-H gel Therefore, self-healing concrete cracks and interfacial transition zones in concrete are considered the most important nanomaterial functionality [25,77,78].

C. Flexure Strength

Guefrech et al. (2011) [80] found that the strength of flexural mortar was enhanced by increasing the nano-silica concentration from 3% to 10%. Similarly, (2015) [81] observed that a 3% nano-silica-]. Guefrech et al. (2011) [80] found that the strength of flexural mortar was enhanced by increasing the nano-silica concentration from 3% to 10%. Similarly, (2015) [81] observed that a 3% nano-silica-modified mortar had the highest flexural strength after undergoing different curing Wu et al. (2019) [81] conducted research to investigate the mechanical behavior of nano-silica carbon fiber-reinforced concrete (NSCFRC) at various temperatures. The study revealed that the optimal concentration for improved flexural strength was 1 wt% nano- silica and 0.15 vol% carbon fiber at room temperature. Additionally, NSCFRC displayed an enhanced residual flexural strength at high temperatures in comparison to carbon fiber concrete. The findings suggest that incorporating nano-silica in carbon-fibered concrete can enhance its flexural properties even after being exposed to high temperatures. The chosen carbon fibers had a diameter of 7 µm and a length of 7 mm.

Although the carbon fibers decrease the compressive strength of CFRC (Carbon Fiber-Reinforced Concrete), they contribute to an increase in the flexural strength of the concrete by reducing crack growth across the crack surface. On the other hand, the addition of nano-silica significantly enhances the mechanical properties of the concrete Abna and Mazloom (2022) [82] analyzed the impact of micro-silica, nano-silica, and polypropylene on the fractural strength of concrete. Their findings indicated that the addition of polypropylene fibers increased the fractural strength and fracture energy of the concrete samples. The optimal ratio of these components for achieving the extreme strength of the fracture and fractural energy was determined to be 5% micro- silica, 0.75% nano-silica, and 0.1% polypropylene. Furthermore, the study included Figure3, which presents the fractural strength values of nano-silica-modified concrete.

Based on the studies, it can be inferred that the incorporation of nano-silica in concrete and mortar can enhance their flexural strength, especially when used in conjunction with other reinforcing constituents. Nevertheless, the ideal concentration of nano-silica may be influenced via different factors such as the water-cement ratio, the duration of curing, and the presence of other strengthening agents.

IV. DURABILITY

A. Chloride Penetration Resistance

Recent research has suggested that the addition of nano-silica to concrete can enhance its durability by reducing the penetration of chloride ions. For example, Ref. [84] observed that nano-silica, even at a low dosage of 0.3%, exhibited pozzolanic properties and filler activity, which led to a decrease in the permeation rate of water and ions of chlorine, as determined via MIP experiments. Similarly, Ref. [42] found that 0.5% of nano-silica could reduce the dispersion amount of chloride ions in concrete with water-to-binder ratios between 0.55 and 0.65, resulting in a more refined microstructure as well as a decrease in the crucial cutoff diameter of pores. By incorporating nano-silica (NS) into concrete, its durability can be enhanced via the reduction in pore size and connectivity. NS fills the gaps between cement particles, leading to a more compact microstructure. Additionally, NS exhibits high reactivity and undergoes pozzolanic reactions with calcium hydroxide, a byproduct of cement hydration. Comparing regular concrete to concrete with NS reveals significant distinctions in their MIP outcomes. The addition of NS induces changes in pore structure, size distribution, total porosity, pore volume, and distribution as well as capillary pore size, leading to a more refined microstructure characterized via reduced porosity and enhanced durability. These studies consistently revealed a reduction in the charge passed in slag concrete, indicating a decrease in the transport of chloride ions.

Lincy et al. (2018) [85] observed that, compared to both micro-silica and the control samples, concrete modified with nano-silica demonstrated significantly greater resistance to chloride ion diffusion. Similarly, Jalal et al. (2015) [66] discovered that incorporating nano-silica and silica fume into (HPSCC) resulted in a reduction in the penetration of chloride ions. Figure 4, presented by Li et al. (2020) [86], shows the chloride penetration of autoclaved concrete at varying nano-silica content. As a result, adding nano-silica to concrete can increase its longevity by decreasing chloride ion diffusion; even a small addition of 0.3% can have a good effect.

B. Sulfate Resistance

Huang et al. (2022) [87] examined the impact of adding 0–1.5 wt.% nano-silica and 0–1.0 vol.% polyvinyl alcohol (PVA) fibers on the sulfate resistance and mechanical prop- erties of fly ash/cement paste hybrids. The study revealed that the addition of PVA and nano-silica fibers improved the mortars’ physical characteristics and sulfate resistance. In comparison to the control group without these components, the hybrids with 1.0 vol.% PVA fibers and 1.5 wt.% nano-silica showed a 90% higher flexural strength after twenty eight days of curing. The compressive and flexural strengths of the cement mortars were significantly greater after 72 days of immersion in the Na2SO4 solution than they were after a total of 28 days of curing. Additionally, mortars containing 1.0–1.5 wt.% nano-silica had greater sulfate resistance after a hundred days in water, showing that the inclusion of nano-silica and PVA fibers can greatly increase resistance to sulfate assault

Li et al. (2019) [88] discovered that combining micro-silica and nano-silica in concrete mixes enhanced the resistance to both sulfate and chloride attacks. The study demonstrated that the use of a combination of micro-silica and nano-silica was more effective in reducing the rate of strength and mass loss of the concrete samples compared to using either silica fume or nano-silica alone. Furthermore, the findings indicated that using micro-silica and nano-silica in concrete mixes resulted in the formation of more dense and compact microstructures, which can increase the strength of concrete to sulfate and chloride attacks.

Huang et al. (2020) [89] discovered that the combination of nano-silica in cement pastes improved their resistance to sulfate and that the level of improvement rose as the concentration of nano-silica enlarged. They also discovered that the addition of coarse nano- silica was more active than fine nano-silica in improving sulfate resistance, presumably due to its superior filling capacity forvoids in the cement matrix. Using a range of analytical methods, the study examined the microstructure and phase composition of the damaged specimens, providing a better understanding of the mechanisms underlying the improved sulfate resistance Previous studies have indicated that the inclusion of nano-silica in other cementitious materials, such as silica fumes, can improve the concrete’s resistance to sulfate and chloride attacks. The addition of nano-silica is thought to refine the pore structure of the cement matrix, reduce pore connectivity, and enhance sulfate resistance. Furthermore, the efficacy of nano-silica in improving sulfate resistance may be influenced via its particle size, as coarse nano-silica particles have been found to be more effective than fine nano-silica particles in enhancing the sulfate resistance of cement mortars

C. Water Absorption

Rajput & Pimplikar (2022) [90] conducted research which showed that increasing the concentration of nano-silica in M30 and M40 grade concretes decreased the absorption of water. The absorption of water from the M30 concrete reduced by 5.15%, 30.15%, and 35.66% compared to the control mix, as the concentration of nano-silica increased from 1% to 3%. For the M40 concrete, the water absorption decreased by 1.47%, 30.40%, and 58.97% when 1%, 2%, and 3% of nano-silica content was added, respectively. The addition of nano-silica to the cement composites improved the pore structure, resulting in reduced water absorption values and improved durability. Athira and Shanmugapriya (2022) [91] investigated the potential of using calcined red mud cement pastes with and without colloidal nano-silica (CNS) at different (W/B ratios).  They found that the incorporation of 1.5% CNS into red mud cement paste led to decreased water absorption at all W/B ratios, indicating that adding nano-silica can enhance the durability of cement-based materials

According to [67], the inclusion of nano-silica in UHPC can decrease its water sorptivity and absorption. This effect is due to the high pozzolanic reactivity of nano-silica, which leads to the formation of more hydration products that fill the capillary pores and reduce their connectivity.

In general, the studies reviewed suggest that incorporating nano-silica into concrete can improve its pore structure, leading to lower water absorption and greater resistance to sulfate and acid attacks. Additionally, the pozzolanic reaction of nano-silica can decrease the connectivity of capillary pores by filling them with more hydration products, which can further enhance the concrete’s durability by reducing water sorptivity and absorption.

D. Carbonation Resistance

According to several studies, adding nanomaterials may increase the concrete’s resis- tance to carbonation. Li et al. (2017) [92] examined the influence of micro- and nano-silica on carbonation in concrete. The research found that adding both micro- and nano-silica to concrete can decrease carbonation, with the best results achieved when both additives were used together. The study also indicated that substituting 10% of micro-silica had a larger influence on reducing carbonation penetration than substituting1% of nano-silica.

Kumar et al. (2019) [56] found that the addition of up to 3% micro-silica to regular concrete resulted in a reduction in carbonation depth by 46% and 17% after 7 and 70 days, respectively. However, increasing the amount of micro-silica beyond 3% resulted in an increase in carbonation depth over time. The study suggests that the combination of sufficient calcium hydroxide (CH) and 3% micro-silica can result in the development of C-S-H gel and a thicker matrix of concrete. However adding more than 3% micro-silica did not lead to a denser concrete matrix.

Isfahani et al. (2016) [42] looked into the effects of various nano-silica doses on the carbonation resistance of concrete with various water-to-binder (w/b) ratios and discovered various outcomes.

Contrary to other studies, the authors found that adding more nano- silica did not increase the resistance of carbonation for concrete with 0.65 and 0.50 water- cement ratios. The study concluded that the w/b ratio is more important than nano-silica in improving the concrete’s carbonation resistance, and adding more nano-silica could have an undesirable influence on the resistance of carbonation.

To note, the influence of nano-silica on carbonation resistance can differ based on the concrete mix and environmental conditions, as per previous studies. While some studies showed that adding nano-silica can enhance carbonation resistance, others observed little or negative effects.

Factors like the dosage and type of nano-silica, w/c ratio, and curing conditions need to be considered when evaluating the possible impact of nano-silica on carbonation resistance. More research is necessary to establish the ideal conditions for using nano-silica to boost carbonation resistance in concrete.

Conclusion

In a review of around one hundred recent and past studies, it was found that increasing the amount of nano-silica in concrete enhances its compressive, split tensile, and flexural strength. This is due to the activator role of nano-silica in promoting hydration and im- proving microstructural pore density. Additionally, by raising the density of the interfacial transition zone (ITZ), nano-silica enhances the concrete matrix’s resilience. However, due to issues such as agglomeration formation, high cost, and restricted availability in some areas, the use of nano-silica in the manufacturing of concrete is not commonly adopted. Another major worry is the ineffective distribution of nano-silica in concrete. While sonication is a viable remedy, further analysis is required to resolve this problem. Although nano-silica has been extensively researched, its commercial use in the construction industry is still in the early stages, and large-scale application remains limited: 1) By considering various factors such as the nature and dimensions of the nano-silica dosage, dispersion technique, dispersant type, water-cement ratio, and sequence of mixing, it becomes possible to discern the impact on the strength of concrete. 2) Inadequate dispersion or an increase in nucleation sites that can generate C-S-H gel due to the pozzolanic reaction can result in agglomeration when nano-silica has a high specific surface area. The dispersion method and type of dispersant used are factors that influence this 3) The recommended replacement dose of nano-silica varies between 2 and 3%, according to the kind of cement used 4) In order to retain the rolling effect of nano-silica and prevent the decrease in concrete workability, it might be essential to employ a significant quantity of plasticizers and elevate the water-cement ratio. 5) Nano-silica can enhance compressive strength while significantly improving other ductile properties, making it suitable to blend with fibers to further enhance ductility. 6) At the optimal dosage, the durability of nano-silica-modified concrete can be sig- inefficiently improved. This is due to the stable hydration products generated in the pozzolanic process, which resist the ingress of harmful chemicals that cause degradation.

References

[1] Crainic, N.; Marques, A.T. Nanocomposites: A State-of-the-Art Review. Key Eng. Mater. 2002, 230–232, 656. [CrossRef] [2] Mehta, P.K.; Monteiro, P.J. Concrete: Microstructure, Properties, and Materials; McGraw-Hill Education: New York, NY, USA, 2014. [3] Zhao, S.; Sun, W. Nano-mechanical behavior of a green ultra-high performance concrete. Constr. Build. Mater. 2014, 63, 150–160. [CrossRef] [4] Wang, C.; Yang, C.; Liu, F.; Wan, C.; Pu, X. Preparation of Ultra-High Performance Concrete with common technology and materials. Cem. Concr. Compos. 2012, 34, 538–544. [CrossRef] [5] Rashad, A.M. Metakaolin as cementitious material: History, scours, production and composition—A comprehensive overview. Constr. Build. Mater. 2013, 41, 303–318. [CrossRef] [6] Güneyisi, E.; Gesog? lu, M.; Karaog? lu, S.; Mermerdas¸, K. Strength, permeability and shrinkage cracking of silica fume and metakaolin concretes. Constr. Build. Mater. 2012, 34, 120–130. [CrossRef] [7] Han, B.; Ding, S.; Wang, J.; Ou, J.; Han, B.; Ding, S.; Wang, J.; Ou, J. Current Progress of Nano-Engineered Cementitious Composites. In Nano-Engineered Cementitious Composites: Principles and Practices; Springer: Singapore, 2019; pp. 97–398. [8] Cui, Y.; Kundalwal, S.; Kumar, S. Gas barrier performance of graphene/polymer nanocomposites. Carbon 2016, 98, 313–333. [CrossRef] [9] Han, B.; Wang, Y.; Dong, S.; Zhang, L.; Ding, S.; Yu, X.; Ou, J. Smart concretes and structures: A review. J. Intell. Mater. Syst. Struct. 2015, 26, 1303–1345. [CrossRef] [10] García-Macías, E.; D’Alessandro, A.; Castro-Triguero, R.; Pérez-Mira, D.; Ubertini, F. Micromechanics modeling of the uniaxial strain-sensing property of carbon nanotube cement-matrix composites for SHM applications. Compos. Struct. 2017, 163, 195–215. [CrossRef] [11] Shi, C.; Zheng, K. A review on the use of waste glasses in the production of cement and concrete. Resour. Conserv. Recycl. 2007, 52, 234–247. [CrossRef] [12] Kong, D.; Du, X.; Wei, S.; Zhang, H.; Yang, Y.; Shah, S.P. Influence of nano-silica agglomeration on microstructure and properties of the hardened cement-based materials. Constr. Build. Mater. 2012, 37, 707–715. [CrossRef] [13] Tobón, J.I.; Payá, J.; Restrepo, O.J. Study of durability of Portland cement mortars blended with silica nanoparticles. Constr. Build. Mater. 2015, 80, 92–97. [CrossRef] [14] Güneyisi, E.; Atewi, Y.R.; Hasan, M.F. Fresh and rheological properties of glass fiber reinforced self-compacting concrete with nanosilica and fly ash blended. Constr. Build. Mater. 2019, 211, 349–362. [CrossRef] [15] Chandra, C.J.; Shadiya, M.; Bipinbal, P.; Narayanankutty, S.K. Effect of Olivine Nanosilica on the Reinforcement of Natural Rubber Nanosilica Composites. Mater. Today Proc. 2019, 9, 127–132. [CrossRef] [16] Barbhuiya, G.H.; Moiz, M.A.; Hasan, S.D.; Zaheer, M.M. Effects of the nanosilica addition on cement concrete: A review. Mater. Today Proc. 2020, 32, 560–566. [CrossRef] [17] Mebert, A.M.; Baglole, C.J.; Desimone, M.F.; Maysinger, D. Nanoengineered silica: Properties, applications and toxicity. Food Chem. Toxicol. 2017, 109, 753–770. [CrossRef] [18] Behzadian, R.; Shahrajabian, H. Experimental Study of the Effect of Nano-silica on the Mechanical Properties of Concrete/PET Composites. KSCE J. Civ. Eng. 2019, 23, 3660–3668. [CrossRef] [19] Li, L.G.; Zheng, J.Y.; Zhu, J.; Kwan, A.K.H. Combined usage of micro-silica and nano-silica in concrete: SP demand, cementing efficiencies and synergistic effect. Constr. Build. Mater. 2018, 168, 622–632. [CrossRef] [20] Ren, J.; Lai, Y.; Gao, J. Exploring the influence of SiO2 and TiO2 nanoparticles on the mechanical properties of concrete. Constr. Build. Mater. 2018, 175, 277–285. [CrossRef] [21] Reches, Y. Nanoparticles as concrete additives: Review and perspectives. Constr. Build. Mater. 2018, 175, 483–495. [CrossRef] [22] Wang, X.; Huang, Y.; Wu, G.; Fang, C.; Li, D.; Han, N.; Xing, F. Effect of nano-SiO2 on strength, shrinkage and cracking sensitivity of lightweight aggregate concrete. Constr. Build. Mater. 2018, 175, 115–125. [CrossRef] [23] Ying, J.; Zhou, B.; Xiao, J. Pore structure and chloride diffusivity of recycled aggregate concrete with nano-SiO2 and nano-TiO2. Constr. Build. Mater. 2017, 150, 49–55. [CrossRef] [24] Ardalan, R.B.; Jamshidi, N.; Arabameri, H.; Joshaghani, A.; Mehrinejad, M.; Sharafi, P. Enhancing the permeability and abrasion resistance of concrete using colloidal nano-SiO2 oxide and spraying nanosilicon practices. Constr. Build. Mater. 2017, 146, 128–135. [CrossRef] [25] Xu, J.; Wang, B.; Zuo, J. Modification effects of nanosilica on the interfacial transition zone in concrete: A multiscale approach. Cem. Concr. Compos. 2017, 81, 1–10. [CrossRef] [26] Sharkawi, A.M.; Abd-Elaty, M.A.; Khalifa, O.H. Synergistic influence of micro-nano silica mixture on durability performance of cementious materials. Constr. Build. Mater. 2018, 164, 579–588. [CrossRef] [27] Norhasri, M.M.; Hamidah, M.S.; Fadzil, A.M. Applications of using nano material in concrete: A review. Constr. Build. Mater. 2017, 133, 91–97. [CrossRef] [28] Mohammed, B.S.; Liew, M.S.; Alaloul, W.S.; Khed, V.C.; Hoong, C.Y.; Adamu, M. Properties of nano-silica modified pervious concrete. Case Stud. Constr. Mater. 2018, 8, 409–422. [CrossRef] [29] Dingreville, R.; Qu, J.; Cherkaoui, M. Surface free energy and its effect on the elastic behavior of nano-sized particles, wires and films. J. Mech. Phys. Solids 2005, 53, 1827–1854. [CrossRef] [30] Koutsawa, Y.; Tiem, S.; Yu, W.; Addiego, F.; Giunta, G. A micromechanics approach for effective elastic properties of nano- composites with energetic surfaces/interfaces. Compos. Struct. 2017, 159, 278–287. [CrossRef] [31] Li, H.; Xiao, H.-G.; Ou, J.-P. A study on mechanical and pressure-sensitive properties of cement mortar with nanophase materials. Cem. Concr. Res. 2004, 34, 435–438. [CrossRef] [32] Teng, X.; Liu, H.; Huang, C. Effect of Al2O3 particle size on the mechanical properties of alumina-based ceramics. Mater. Sci. Eng. A 2007, 452–453, 545–551. [CrossRef] [33] Amin, M.; Abu el-Hassan, K. Effect of using different types of nano materials on mechanical properties of high strength concrete. Constr. Build. Mater. 2015, 80, 116–124. [CrossRef] [34] Zhao, Z.R.; Kong, J.; Yang, H.X. Study on Frost Resistance of Nano SiO2 Cement Concrete. Appl. Mech. Mater. 2012, 198–199, 48–51. [CrossRef] [35] Shaikh, F.U.; Supit, S.W. Mechanical and durability properties of high volume fly ash (HVFA) concrete containing calcium carbonate (CaCO3) nanoparticles. Constr. Build. Mater. 2014, 70, 309–321. [CrossRef] [36] Chithra, S.; Kumar, S.S.; Chinnaraju, K. The effect of Colloidal Nano-silica on workability, mechanical and durability properties of High Performance Concrete with Copper slag as partial fine aggregate. Constr. Build. Mater. 2016, 113, 794–804. [CrossRef] [37] Salemi, N.; Behfarnia, K. Effect of nano-particles on durability of fiber-reinforced concrete pavement. Constr. Build. Mater. 2013, 48, 934–941. [CrossRef] [38] Mohamed, A.M. Influence of nano materials on flexural behavior and compressive strength of concrete. HBRC J. 2016, 12, 212–225. [CrossRef] [39] Wu, Z.; Shi, C.; Khayat, K.; Wan, S. Effects of different nanomaterials on hardening and performance of ultra-high strength concrete (UHSC). Cem. Concr. Compos. 2016, 70, 24–34. [CrossRef] [40] Li, W.; Huang, Z.; Cao, F.; Sun, Z.; Shah, S.P. Effects of nano-silica and nano-limestone on flowability and mechanical properties of ultra-high-performance concrete matrix. Constr. Build. Mater. 2015, 95, 366–374. [CrossRef] [41] Gao, Y.; He, B.; Li, Y.; Tang, J.; Qu, L. Effects of nano-particles on improvement in wear resistance and drying shrinkage of road fly ash concrete. Constr. Build. Mater. 2017, 151, 228–235. [CrossRef] [42] Torabian Isfahani, F.; Redaelli, E.; Lollini, F.; Li, W.; Bertolini, L. Effects of nanosilica on compressive strength and durability properties of concrete with different water to binder ratios. Adv. Mater. Sci. Eng. 2016, 2016, 8453567. [CrossRef] [43] Said, A.; Zeidan, M.; Bassuoni, M.; Tian, Y. Properties of concrete incorporating nano-silica. Constr. Build. Mater. 2012, 36, 838–844. [CrossRef] [44] Hosseini, P.; Afshar, A.; Vafaei, B.; Booshehrian, A.; Raisi, E.M.; Esrafili, A. Effects of nano-clay particles on the short-term properties of self-compacting concrete. Eur. J. Environ. Civ. Eng. 2017, 21, 127–147. [CrossRef] [45] Wang, J.L.; Meng, L.J. Influence of Carbon Nano-Fiber on Mechanical Property of PALC. Appl. Mech. Mater. 2014, 535, 785–787. [CrossRef] [46] Saba, N.; Paridah, M.; Abdan, K.; Ibrahim, N. Effect of oil palm nano filler on mechanical and morphological properties of kenaf reinforced epoxy composites. Constr. Build. Mater. 2016, 123, 15–26. [CrossRef] [47] Oh, S.T.; Yoon, S.J.; Choa, Y.H.; Jeong, Y.K.; Niihara, K. Wear behavior of nano-sized metal particle dispersed Al2O3 nanocompos- ites. Key Eng. Mater. 2006, 317, 369–372. [CrossRef] [48] Das, S.; Chandrasekaran, M.; Samanta, S. Comparison of Mechanical properties of AA6061 reinforced with (SiC/B4C) micro/nano ceramic particle reinforcements. Mater. Today Proc. 2018, 5, 18110–18119. [CrossRef] [49] Schmitz, A.; Schmid, C.; de Boor, J.; Mueller, E. Dispersion of multi-walled carbon nanotubes in skutterudites and its effect on thermoelectric and mechanical properties. J. Nanosci. Nanotechnol. 2017, 17, 1547–1554. [CrossRef] [50] Zhu, W.; Huang, J.; Lu, W.; Sun, Q.; Peng, L.; Fen, W.; Li, H.; Ou, Y.; Liu, H.; Wang, D.; et al. Performance test of Nano-HA/PLLA composites for interface fixation. Artif. Cells Nanomed. Biotechnol. 2014, 42, 331–335. [CrossRef] [51] Singh, L.; Ali, D.; Tyagi, I.; Sharma, U.; Singh, R.; Hou, P. Durability studies of nano-engineered fly ash concrete. Constr. Build. Mater. 2019, 194, 205–215. [CrossRef] [52] Mondal, P.; Shah, S.P.; Marks, L.D.; Gaitero, J.J. Comparative Study of the Effects of Microsilica and Nanosilica in Concrete. Transp. Res. Rec. J. Transp. Res. Board 2010, 2141, 6–9. [CrossRef] [53] de Abreu, G.B.; Costa, S.M.M.; Gumieri, A.G.; Calixto, J.M.F.; França, F.C.; Silva, C.; Quinõnes, A.D. Mechanical properties and microstructure of high performance concrete containing stabilized nano-silica. Matéria 2017, 22. [CrossRef] [54] Quercia, G.; Brouwers, H.J.H. Application of nano-silica (nS) in concrete mixtures. In Proceedings of the 8th Fib PhD Symposium in Civil Engineering, Lyngby, Denmark, 20–23 June 2010; pp. 431–436. [55] Senff, L.; Hotza, D.; Repette, W.L.; Ferreira, V.M.; Labrincha, J.A. Mortars with nano-SiO2 and micro-SiO2 investigated by experimental design. Constr. Build. Mater. 2010, 24, 1432–1437. [CrossRef] [56] Kumar, S.; Kumar, A.; Kujur, J. Influence of nanosilica on mechanical and durability properties of concrete. Struct. Build. 2019, 172, 781–788. [CrossRef] [57] Khaloo, A.; Mobini, M.H.; Hosseini, P. Influence of different types of nano-SiO2 particles on properties of high-performance concrete. Constr. Build. Mater. 2016, 113, 188–201. [CrossRef] [58] Singh, L.P.; Bhattacharyya, S.K.; Shah, S.P.; Mishra, G.; Sharma, U. Studies on early stage hydration of tricalcium silicate incorporating silica nanoparticles: Part II. Constr. Build. Mater. 2016, 102, 943–949. [CrossRef] [59] Elkady, H.M.; Yasien, A.M.; Elfeky, M.S.; Serag, M.E. Assessment of mechanical strength of nano silica concrete (NSC) subjected to elevated temperatures. J. Struct. Fire Eng. 2019, 10, 90–109. [CrossRef] [60] Yonggui, W.; Shuaipeng, L.; Hughes, P.; Yuhui, F. Mechanical properties and microstructure of basalt fibre and nano-silica reinforced recycled concrete after exposure to elevated temperatures. Constr. Build. Mater. 2020, 247, 118561. [CrossRef] [61] Alhawat, M.; Ashour, A. Bond strength between corroded steel and recycled aggregate concrete incorporating nano silica. Constr. Build. Mater. 2020, 237, 117441. [CrossRef] [62] Deb, P.S.; Sarker, P.K.; Barbhuiya, S. Effects of nano-silica on the strength development of geopolymer cured at room temperature. Constr. Build. Mater. 2015, 101, 675–683. [CrossRef] [63] Adak, D.; Sarkar, M.; Mandal, S. Effect of nano-silica on strength and durability of fly ash based geopolymer mortar. Constr. Build. Mater. 2014, 70, 453–459. [CrossRef] [64] Their, J.M.; Özakça, M. Developing geopolymer concrete by using cold-bonded fly ash aggregate, nano-silica, and steel fiber. Constr. Build. Mater. 2018, 180, 12–22. [CrossRef] [65] Mustakim, S.M.; Das, S.K.; Mishra, J.; Aftab, A.; Alomayri, T.S.; Assaedi, H.S.; Kaze, C.R. Improvement in Fresh, Mechanical and Microstructural Properties of Fly Ash-Blast Furnace Slag Based Geopolymer Concrete by Addition of Nano and Micro Silica. Silicon 2021, 13, 2415–2428. [CrossRef] [66] Jalal, M.; Pouladkhan, A.; Harandi, O.F.; Jafari, D. RETRACTED: Comparative study on effects of Class F fly ash, nano silica and silica fume on properties of high performance self compacting concrete. Constr. Build. Mater. 2015, 94, 90–104. [CrossRef] [67] Ghafari, E.; Costa, H.; Júlio, E.; Portugal, A.; Durães, L. The effect of nanosilica addition on flowability, strength and transport properties of ultra high performance concrete. Mater. Des. 2014, 59, 1–9. [CrossRef] [68] Fallah, S.; Nematzadeh, M. Mechanical properties and durability of high-strength concrete containing macro-polymeric and polypropylene fibers with nano-silica and silica fume. Constr. Build. Mater. 2017, 132, 170–187. [CrossRef] [69] Hasan-Nattaj, F.; Nematzadeh, M. The effect of forta-ferro and steel fibers on mechanical properties of high-strength concrete with and without silica fume and nano-silica. Constr. Build. Mater. 2017, 137, 557–572. [CrossRef] [70] Mukharjee, B.B.; Barai, S.V. Influence of Incorporation of Colloidal Nano-Silica on Behaviour of Concrete. Iran. J. Sci. Technol. Trans. Civ. Eng. 2020, 44, 657–668. [CrossRef] [71] Nuaklong, P.; Sata, V.; Wongsa, A.; Srinavin, K.; Chindaprasirt, P. Recycled aggregate high calcium fly ash geopolymer concrete with inclusion of OPC and nano-SiO2. Constr. Build. Mater. 2018, 174, 244–252. [CrossRef] [72] Ganesh, P.; Ramachandra Murthy, A.; Sundar Kumar, S.; Mohammed Saffiq Reheman, M.; Iyer, N.R. Effect of nanosilica on durability and mechanical properties of high-strength concrete. Mag. Concr. Res. 2016, 68, 229–236. [CrossRef] [73] Atmaca, N.; Abbas, M.L.; Atmaca, A. Effects of nano-silica on the gas permeability, durability and mechanical properties of high-strength lightweight concrete. Constr. Build. Mater. 2017, 147, 17–26. [CrossRef [74] Mondal, P.; Shah, S.P.; Marks, L.D.; Gaitero, J.J. Comparative Study of the Effects of Microsilica and Nanosilica in Concrete. Transp. Res. Rec. J. Transp. Res. Board 2010, 2141, 6–9. [CrossRef] [75] Mondal, P.; Shah, S.P.; Marks, L.D.; Gaitero, J.J. Comparative Study of the Effects of Microsilica and Nanosilica in Concrete. Transp. Res. Rec. J. Transp. Res. Board 2010, 2141, 6–9. [CrossRef] [76] de Abreu, G.B.; Costa, S.M.M.; Gumieri, A.G.; Calixto, J.M.F.; França, F.C.; Silva, C.; Quinõnes, A.D. Mechanical properties and microstructure of high performance concrete containing stabilized nano-silica. Matéria 2017, 22. [CrossRef] [77] Quercia, G.; Brouwers, H.J.H. Application of nano-silica (nS) in concrete mixtures. In Proceedings of the 8th Fib PhD Symposium in Civil Engineering, Lyngby, Denmark, 20–23 June 2010; pp. 431–436. [78] Senff, L.; Hotza, D.; Repette, W.L.; Ferreira, V.M.; Labrincha, J.A. Mortars with nano-SiO2 and micro-SiO2 investigated by experimental design. Constr. Build. Mater. 2010, 24, 1432–1437. [CrossRef] [79] Kumar, S.; Kumar, A.; Kujur, J. Influence of nanosilica on mechanical and durability properties of concrete. Struct. Build. 2019, 172, 781–788. [CrossRef] [80] Khaloo, A.; Mobini, M.H.; Hosseini, P. Influence of different types of nano-SiO2 particles on properties of high-performance concrete. Constr. Build. Mater. 2016, 113, 188–201. [CrossRef] [81] Singh, L.P.; Bhattacharyya, S.K.; Shah, S.P.; Mishra, G.; Sharma, U. Studies on early stage hydration of tricalcium silicate incorporating silica nanoparticles: Part II. Constr. Build. Mater. 2016, 102, 943–949. [CrossRef] [82] Elkady, H.M.; Yasien, A.M.; Elfeky, M.S.; Serag, M.E. Assessment of mechanical strength of nano silica concrete (NSC) subjected to elevated temperatures. J. Struct. Fire Eng. 2019, 10, 90–109. [CrossRef] [83] Yonggui, W.; Shuaipeng, L.; Hughes, P.; Yuhui, F. Mechanical properties and microstructure of basalt fibre and nano-silica reinforced recycled concrete after exposure to elevated temperatures. Constr. Build. Mater. 2020, 247, 118561. [CrossRef] [84] Alhawat, M.; Ashour, A. Bond strength between corroded steel and recycled aggregate concrete incorporating nano silica. Constr. Build. Mater. 2020, 237, 117441. [CrossRef] [85] Deb, P.S.; Sarker, P.K.; Barbhuiya, S. Effects of nano-silica on the strength development of geopolymer cured at room temperature. Constr. Build. Mater. 2015, 101, 675–683. [CrossRef] [86] Adak, D.; Sarkar, M.; Mandal, S. Effect of nano-silica on strength and durability of fly ash based geopolymer mortar. Constr. Build. Mater. 2014, 70, 453–459. [CrossRef] [87] Their, J.M.; Özakça, M. Developing geopolymer concrete by using cold-bonded fly ash aggregate, nano-silica, and steel fiber. Constr. Build. Mater. 2018, 180, 12–22. [CrossRef] [88] Mustakim, S.M.; Das, S.K.; Mishra, J.; Aftab, A.; Alomayri, T.S.; Assaedi, H.S.; Kaze, C.R. Improvement in Fresh, Mechanical and Microstructural Properties of Fly Ash-Blast Furnace Slag Based Geopolymer Concrete by Addition of Nano and Micro Silica. Silicon 2021, 13, 2415–2428. [CrossRef] [89] Jalal, M.; Pouladkhan, A.; Harandi, O.F.; Jafari, D. RETRACTED: Comparative study on effects of Class F fly ash, nano silica and silica fume on properties of high performance self compacting concrete. Constr. Build. Mater. 2015, 94, 90–104. [CrossRef] [90] Ghafari, E.; Costa, H.; Júlio, E.; Portugal, A.; Durães, L. The effect of nanosilica addition on flowability, strength and transport properties of ultra high performance concrete. Mater. Des. 2014, 59, 1–9. [CrossRef] [91] Fallah, S.; Nematzadeh, M. Mechanical properties and durability of high-strength concrete containing macro-polymeric and polypropylene fibers with nano-silica and silica fume. Constr. Build. Mater. 2017, 132, 170–187. [CrossRef] [92] Hasan-Nattaj, F.; Nematzadeh, M. The effect of forta-ferro and steel fibers on mechanical properties of high-strength concrete with and without silica fume and nano-silica. Constr. Build. Mater. 2017, 137, 557–572. [CrossRef] [93] Mukharjee, B.B.; Barai, S.V. Influence of Incorporation of Colloidal Nano-Silica on Behaviour of Concrete. Iran. J. Sci. Technol. Trans. Civ. Eng. 2020, 44, 657–668. [CrossRef] [94] Nuaklong, P.; Sata, V.; Wongsa, A.; Srinavin, K.; Chindaprasirt, P. Recycled aggregate high calcium fly ash geopolymer concrete with inclusion of OPC and nano-SiO2. Constr. Build. Mater. 2018, 174, 244–252. [CrossRef] [95] Ganesh, P.; Ramachandra Murthy, A.; Sundar Kumar, S.; Mohammed Saffiq Reheman, M.; Iyer, N.R. Effect of nanosilica on durability and mechanical properties of high-strength concrete. Mag. Concr. Res. 2016, 68, 229–236. [CrossRef] [96] Atmaca, N.; Abbas, M.L.; Atmaca, A. Effects of nano-silica on the gas permeability, durability and mechanical properties of high-strength lightweight concrete. Constr. Build. Mater. 2017, 147, 17–26. [CrossRef] [97] Supit, S.W.M.; Shaikh, F.U.A. Durability properties of high volume fly ash concrete containing nano-silica. Supit, S.W.M.; Shaikh, F.U.A. Durability properties of high volume fly ash concrete containing nano-silica. Mater. Struct. 2015, 48, 2431–2445. [CrossRef] [98] Beigi, M.H.; Berenjian, J.; Omran, O.L.; Nik, A.S.; Nikbin, I.M. An experimental survey on combined effects of fibers and nanosilica on the mechanical, rheological, and durability properties of self-compacting concrete. Mater. Des. 2013, 50, 1019–1029. [CrossRef] [99] Zhang, A.; Ge, Y.; Yang, W.; Cai, X.; Du, Y. Comparative study on the effects of nano-SiO2, nano-Fe2O3 and nano-NiO on hydration and microscopic properties of white cement. Constr. Build. Mater. 2019, 228, 116767. [CrossRef] [100] Wang, X.; Xu, J.; Wang, Z.; Yao, W. Use of recycled concrete aggregates as carriers for self-healing of concrete cracks by bacteria with high urease activity. Constr. Build. Mater. 2022, 337, 127581. [CrossRef] [101] Zhan, P.; Xu, J.; Wang, J.; Zuo, J.; He, Z. A review of recycled aggregate concrete modified by nanosilica and graphene oxide: Materials, performances and mechanism. J. Clean. Prod. 2022, 375, 134116. [CrossRef] [102] Varghese, L.; Rao, V.V.L.K.; Parameswaran, L. Nanosilica-added concrete: Strength and its correlation with time-dependent properties. Proc. Inst. Civ. Eng.-Constr. Mater. 2019, 172, 85–94. [103] Ltifi; Guefrech, A.; Mounanga, P.; Khelidj, A. Experimental study of the effect of addition of nano-silica on the behaviour of cement mortars Mounir. Procedia Eng. 2011, 10, 900–905. [CrossRef]